MIL-DTL-14067C
3. REQUIREMENTS
3.1 Required inspections.
3.1.1 First article. When specified (see 6.2), a sample shall be subjected to first article
inspection in accordance with 4.2.
3.1.2 Conformance. A sample shall be subject to conformance inspection in accordance
with 4.3.
3.2 Material. Type I, III and IV magnesium powder shall be manufactured from
magnesium ingot or stick that meets the requirements of ASTM B92M.
3.3 Shape.
3.3.1 Shape - Type I, III and V. The shape of the metal powders Type I, III and V
particles shall be spheroidal (see 6.3).
3.3.2 Shape - Type II. The shape of the metal powders atomized Type II particles shall
be spheroidal or granular (see 6.3).
3.3.3 Shape - Type IV. The shape of the ellipsoidal magnesium shall be spheroidal with
a maximum of 30 percent oblong shape particles (see 6.3).
3.4 Chemical and physical properties. The metal powder shall conform to the chemical
and physical requirements as shown in Table I.
3.4.1 Magnesium. The magnesium shall conform to the chemical and physical
requirements as shown in Table I.
3.4.2 Aluminum. The aluminum shall conform to the chemical and physical
requirements as shown in Table I.
3.4.3 Volatile material at 105o C. The volatile material at 105o C shall conform to the
chemical and physical requirements as shown in Table I.
3.4.4 Oil and grease. The oil and grease shall conform to the chemical and physical
requirements as shown in Table I.
3.4.5 Zinc. The zinc shall conform to the chemical and physical requirements as shown
in Table I.
3.4.6 Silicon. The silicon shall conform to the chemical and physical requirements as
shown in Table I.
3